The invention claimed is:
1. Desiccant clay-bound zeolite, which comprises zeolite, clay and hygroscopic salt, and optionally further additives, wherein the desiccant is in the form of granules and the hygroscopic salt is present in the pores of the granules but does not fill the micropores of the zeolite.
2. Desiccant according to claim 1, wherein the zeolite comprises sodium-containing zeolite of the structure type A, potassium-containing zeolite of the structure type A, zeolite of the faujasite structure type or a mixture thereof.
3. Desiccant according to claim 1, wherein the zeolite comprises potassium-containing zeolite of the structure type A.
4. Desiccant according to claim 2, wherein the potassium-containing zeolite of the structure type A has a potassium content of 9 to 18 wt. % (relative to the weight of the zeolite).
5. Desiccant according to one of claims 1, wherein the clay comprises montmorillonite, kaolinite, bentonite, smectite, attapulgite, sepiolite or a mixture thereof.
6. Desiccant according to one of claims 1, wherein the hygroscopic salt comprises magnesium chloride, calcium chloride, magnesium sulphate, sodium sulphite, magnesium polyphosphate, sodium polyphosphate, sodium carbonate, sodium sulphate or a mixture thereof.
7. Desiccant according to claim 6, wherein the hygroscopic salt is selected from magnesium chloride, magnesium sulphate and magnesium polyphosphate.
8. Desiccant according to claim 7, wherein the hygroscopic salt is magnesium sulphate.
9. Desiccant according to one of claims 1, which comprises 50 to 90 wt. -% zeolite, 5 to 40 wt. -% clay, 2 to 30 wt. -% hygroscopic salt and optionally 0 to 5 wt. % further additives.
10. Desiccant according to one of claim 1, which has a water-absorption capacity (measured at 10% relative humidity and 25.degree. C.) of 18 wt .-% or greater, relative to the weight of the desiccant, a bulk density of 800 g/l or greater, and a water-absorption capacity per volume of 160 g H.sub.2O/1 desiccant or greater.
11. Process for the preparation of a desiccant according to one of claims 1, wherein a starting mixture comprising the components (a) zeolite, (b) clay, (c) hygroscopic salt and (d) optionally further additives is mixed, aggregated and the product obtained by aggregation is activated, optionally after drying and/or sieving.
12. Process according to claim 11, wherein a starting mixture is aggregated by granulation using granulation liquid (wet granulation).
13. Process according to claim 12, wherein a solvent or solvent mixture is used as granulation liquid.
14. Process according to claim 13, wherein a solvent or suspension of part or all of the hygroscopic salt (component (c)) of the starting mixture in the solvent or solvent mixture is used as granulation liquid.
15. Process according to claim 14, wherein the starting mixture comprising the components zeolite, clay and optionally further additives is wet-granulated using a solution or suspension of hygroscopic salt in a solvent or solvent mixture and then the granules obtained are activated, optionally after the drying and/or sieving.
16. Process according to claim 15, wherein an aqueous solution of one or more hygroscopic salt(s) is used as granulation liquid.
17. Process according to claim 16, characterized in that the aqueous solution of one or more hygroscopic salt(s) has a concentration of 10 to 50 wt.-% (relative to the weight of the solution) and/or comprises a saturated aqueous solution of a one or more hygroscopic salt(s).
18. Process according to claim 17, wherein a saturated aqueous magnesium sulphate solution is used as granulation liquid.
19. Insulating glass window or composite window, which comprises desiccant according to one of claims 1.
20. Spacer for insulating glass windows or composite windows, which comprises desiccant according to one of claims 1.
21. Desiccant according to claim 1, which has a water-absorption capacity (measured at 10% relative humidity and 25.degree. C. of 18 wt. -% to 22 wt. -%, (relative to the weight of the desiccant), a bulk density of 800 to 1000 g/l, and a water-absorption capacity per volume of 160 to 180 g H.sub.2O desiccant.
22. Desiccant clay-bound zeolite, which comprises zeolite, clay and hygroscopic salt, and optionally further additives, wherein said desiccant possesses a water absorption capacity (measured at 10% relative humidity and 25.degree. C.) of 18 wt % or greater based on the weight of the desiccant.
23. A mixture comprising zeolite, clay and hygroscopic salt, and optionally further additives, wherein said hygroscopic salt is in solution or suspension. |